HEMPADUR海虹油漆15590老人牌15599

使用微信扫描二维码分享朋友圈，成交更快更简单！

HEMPADUR海虹油漆15590老人牌15599

HEMPADUR 1559015590: BASE 15599: CURING AGENT 95100



Description: Recommended use: Service temperature: Certificates/Approvals: Availability: HEMPADUR 15590 is a two-component epoxy primer coating especially for use on surfaces exposed to severe abrasion. As a blast primer for heavy duty epoxy systems on submerged and non-submerged areas according to specification. For use at temperatures of 5°C/41°F, preferably 10°C/50°F or higher. Maximum, dry exposure only: 140°C/284°F Part of Group Assortment. Local availability subject to confirmation. HEMPADUR 15590 15590: BASE 15599: CURING AGENT 95100 Product Data PHYSICAL CONSTANTS: The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. Shade nos/Colours: Finish: Volume solids, %: Theoretical spreading rate: VOC content: Fully cured: Dry to touch: Specific gravity: Flash point: - 56880 / Red. Semi-gloss 44 ± 1 11 m2 /l [441.1 sq.ft./US gallon] - 40 micron/1.6 mils 3 approx. hour(s) 20°C/68°F 7 day(s) 20°C/68°F 26 °C [78.8 °F] 1.3 kg/litre [11 lbs/US gallon] 498 g/l [4.1 lbs/US gallon] Shelf life: 1 year for BASE and 3 years for CURING AGENT (stored in closed container) (25°C/77°F) from time of production. Depending on storage conditions, mechanical stirring may be necessary before usage. APPLICATION DETAILS: Version, mixed product: Mixing ratio: Application method: Thinner (max.vol.): 15590 15 : 4 by volume Airless spray / Air spray 08450 (5%) / 08450 (15%) Pot life: Nozzle orifice: 2 hour(s) 20°C/68°F 0.017 - 0.019 " Nozzle pressure: 150 bar [2175 psi] (Airless spray data are indicative and subject to adjustment) Indicated film thickness, dry: 40 micron [1.6 mils] Indicated film thickness, wet: 100 micron [4 mils] Overcoat interval, min: see REMARKS overleaf Overcoat interval, max: see REMARKS overleaf BASE 15599: CURING AGENT 95100 Safety: Handle with care. Before and during use, observe all safety labels on packaging and paint containers, consult HEMPEL Safety Data Sheets and follow all local or national safety regulations. Cleaning of tools: HEMPEL'S TOOL CLEANER 99610 - -



​SURFACE PREPARATION: New steel: Remove oil and grease etc. thoroughly with suitable detergent. Remove salts and other contaminants by high pressure fresh water cleaning. Abrasive blasting to Sa 2½-3 (ISO 8501-1:2007) depending on area of use. Minimum surface profile corresponding to Rugotest No. 3, BN11a, KeaneTator Comparator, 5.5 G/S, or ISO Comparator Coarse (G) - or as per specification for the subsequent coat(s). After blasting, clean the surface carefully from abrasives and dust. Repair and maintenance: Remove oil and grease etc. thoroughly with suitable detergent. Remove salts and other contaminants by high pressure fresh water cleaning. On pit-corroded surfaces, excessive amounts of salt residues may call for high pressure water jetting, wet abrasive blasting or, alternatively, dry abrasive blasting, high pressure fresh water hosting, drying, and finally dry abrasive blasting again. APPLICATION CONDITIONS: Apply only on a dry and clean surface with a temperature above the dew point to avoid condensation. Minimum temperature for application is 5°C/41°F, preferably above 10°C/50°F. Relative humidity maximum 80 %, preferably below 60%. The temperature of the paint itself should be: Between 15°C (59°F) and 25°C (77°F). In confined spaces provide adequate ventilation during application and drying. PRECEDING COAT: SUBSEQUENT COAT: None. Recommended systems are: HEMPADUR MULTI-STRENGTH 35530, HEMPADUR MULTISTRENGTH 45751. HEMPADUR 15590 can be used as a blast primer. REMARKS: Film thicknesses/thinning: May be specified in another film thickness than indicated depending on purpose and area of use. This will alter spreading rate and may influence drying time and recoating interval. Normal range dry is: 30-50 micron/1.2-2 mils. Note: HEMPADUR 15590 For professional use only. Overcoating: Overcoating intervals related to later conditions of exposure: If the maximum overcoating interval is exceeded, roughening of the surface is necessary to ensure intercoat adhesion. Before overcoating after exposure in contaminated environment, clean the surface thoroughly with high pressure fresh water hosing and allow drying. A specification supersedes any guideline overcoat intervals indicated in the table. X Move PDS Disclaimer to Second page Overcoating note: The coating is to be applied in a dry film thickness as near as possible to the specified: 40 micron. Film formation of each coat has to be of good quality, free from defects such as pinholes and without any dry spray. Drying and curing conditions have to be according to APPLICATION CONDITIONS until full curing has been obtained. No kind of surface contamination must exist except loose dust, abrasives, loose dry-spray, which is possible to remove by vacuum cleaning before overcoating. The surface MUST be completely clean before overcoating. The coating is to be checked carefully and should have no patchy, whitish, and/or greasy formation, which can hinder adhesion of the subsequent coat. Exudation of the curing agent causes the mentioned patchy, whitish, and/or greasy formation, which will take place if the product is applied at low temperatures without proper induction time and/or if the coating is exposed to water (rain, condensation) during drying and curing. Overcoating intervals: According to specification. The stated minimum overcoating interval may be halved for areas not intended for water immersion. Depending on actual local conditions, extended maximum overcoating interval may apply. Contact Hempel for more information. If the maximum over coating interval is exceeded, roughening of the surface is necessary to ensure intercoat adhesion. Before overcoating after exposure in contaminated environment, clean the surface thoroughly by high pressure water cleaning and allow drying. Theoduct will resist a hosing down of the surface 8 hours after application at a steel temperature of 20°C/68°F. Overcoating intervals: ISSUED BY: HEMPEL A/S